FLEXI-DECK 500-E
100% SOLIDS ELASTOMERIC EPOXY COATING
Edison FLEXI-DECK 500-E
is a 100% solids modified epoxy elastomeric membrane/coating designed for high performance waterproofing, chemical resistance and traffic compatibility under a wide range of application and service conditions.
FLEXI-DECK 500-E
features odorless application, "zero" VOC content, low viscosity and self-priming to concrete, steel, aluminum, ceramic tile*, plywood, natural stone, glass*,
vinyl tile and many other substrates. (*Note: Some glassy surfaces require use of adhesion-promoting additives.)
Clear or a wide range of colors is available.
Common uses for FLEXI-DECK 500-E include:
- PARKING DECK WATERPROOFING MEMBRANES
- INDUSTRIAL FLOORING UNDERLAYMENT
- MECHANICAL ROOM FLOORING NON-SLIP SURFACING
- TANK LINING/SECONDARY CONTAINMENT
THINNING, MIXING & APPLICATION
Surface Preparation: Surfaces to be coated are best if clean and dry, and free of grease, oil, dirt and other
contaminants. If product will he applied over smooth or previously coated surfaces, a test application should be performed to assure adhesion and compatibility. For specific alternate procedures for contaminated or
coated surfaces, consult your Edison Coatings Representative. Detailing of cracks, joints, drains, perimeters and penetrations should be performed as stated in the FLEXI-DECK 500 installation manual.
Thinning & Mixing:FLEXI-DECK 500-E
is supplied as a low viscosity, two-component, 100% solids coating. For most applications, no thinning is required. In some cases thinning may be economically advantageous, to increase product spread rate. In other cases, slight solvent addition may improve the "bite" on a bard existing coating or may improve penetration of slightly oily surfaces. Thinning should be limited to the minimum required, typically about 5 - 10% solvent addition should be sufficient. Use only compatible solvents, such as Edison
FLEXI-THIN 597.
Mix ratio is nominally 1:1 resin to hardener by volume. Measure and mix consistently. Product is also available in
pre-measured units, eliminating the need for field measuring measuring of components. Mix thoroughly for at least two minutes, scraping the container bottom and sides to assure complete mixing. There is no induction
or waiting time required after mixing before application.
The exothermic nature of epoxy setting reactions may cause rapid temperature rise when the mixture is left massed in
a bucket, resulting in high temperatures and loss of utility of the product. To maximize handling and working time, pour the mixture into shallow pans or dump and squeegee tile mixture out onto the surface to be
coated within a few minutes of mixing.
TECHNICAL DATA:
|